prikaz prve stranice dokumenta Influence of phosphate layer on adhesion properties between a steel surface and an organic coating
  Preuzmi
PDF 3.58 MB
Znanstveni rad - Prethodno/kratko priopćenje
Influence of phosphate layer on adhesion properties between a steel surface and an organic coating
Rudarsko-geološko-naftni zbornik, 37 (2022), 1; 11-17. https://doi.org/10.17794/rgn.2022.1.2
Samardžija, Marina; Alar, Vesna; Aljinović, Fedor; Kapor, Frankica

Citirajte ovaj rad

Samardžija, M., Alar, V., Aljinović, F. i Kapor, F. (2022). Influence of phosphate layer on adhesion properties between a steel surface and an organic coating. Rudarsko-geološko-naftni zbornik, 37. (1), 11-17. doi: 10.17794/rgn.2022.1.2

Samardžija, Marina, et al. "Influence of phosphate layer on adhesion properties between a steel surface and an organic coating." Rudarsko-geološko-naftni zbornik, vol. 37, br. 1, 2022, str. 11-17. https://doi.org/10.17794/rgn.2022.1.2

Samardžija, Marina, Vesna Alar, Fedor Aljinović i Frankica Kapor. "Influence of phosphate layer on adhesion properties between a steel surface and an organic coating." Rudarsko-geološko-naftni zbornik 37, br. 1 (2022): 11-17. https://doi.org/10.17794/rgn.2022.1.2

Samardžija, M., et al. (2022) 'Influence of phosphate layer on adhesion properties between a steel surface and an organic coating', Rudarsko-geološko-naftni zbornik, 37(1), str. 11-17. doi: 10.17794/rgn.2022.1.2

Samardžija M, Alar V, Aljinović F, Kapor F. Influence of phosphate layer on adhesion properties between a steel surface and an organic coating. Rudarsko-geološko-naftni zbornik [Internet]. 2022. [pristupljeno 24.04.2025.];37(1):11-17. doi: 10.17794/rgn.2022.1.2

M. Samardžija, V. Alar, F. Aljinović i F. Kapor, "Influence of phosphate layer on adhesion properties between a steel surface and an organic coating", Rudarsko-geološko-naftni zbornik, vol. 37, br. 1, str. 11-17, 2022. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:169:262362. [Citirano: 24.04.2025.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:169:262362
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)Influence of phosphate layer on adhesion properties between a steel surface and an organic coating
Naslov (hrvatski)Utjecaj fosfatnoga sloja na svojstva prianjanja između čelične površine i organskoga premaza
AutorMarina Samardžija
AutorVesna Alar
AutorFedor Aljinović
AutorFrankica Kapor
Autorova ustanovaSveučilište u Zagrebu
Fakultet strojarstva i brodogradnje
Autorova ustanovaSveučilište u Zagrebu
Rudarsko-geološko-naftni fakultet
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Interdisciplinarne tehničke znanosti
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Kemijsko inženjerstvo
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Rudarstvo, nafta i geološko inženjerstvo
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Strojarstvo
Sažetak (engleski)
In this paper, tests of some physico-chemical properties of protective epoxy coating on non-alloy structural steel grade type S235JRG2 have been carried out. This is a significant construction material whose use is remarkably important for many steel products such as H beam, I beam, transmission towers, steel pipe etc. Coatings represent one of the ways to protect metal from corrosion. The properties of coating thickness, hardness, gloss, and adhesion were investigated. The same properties were tested by exposing the sample non-alloy steel plates to corrosive conditions of the salt and humid chamber and seawater. Part of the samples prior to application of the coating were immersed to phosphate solution to further investigate the effects of phosphatization on the properties of the coating. After exposure of the plates to the humidity chamber conditions, no traces of corrosion products, cracking or peeling of the coating were found on the surfaces. The plates tested in the sea water and salt chamber showed a minor damage on protective coating. The traitability properties were tested by the Pull off Adhesion test. Force pull adhesion off test shows less value for unphosphated samples than for phosphated ones.
Sažetak (hrvatski)
U ovome radu provedena su ispitivanja nekih fizičko-kemijskih svojstava zaštitne epoksidne prevlake na nelegiranome strukturnom čeliku tipa S235JRG2. To je bitan konstrukcijski materijal čija je upotreba iznimno važna za mnoge proizvode od čelika poput H nosača, I nosača, prijenosnih tornjeva, čeličnih cijevi i slično. Jedna od najčešćih metoda zaštite metala od korozije jesu organski premazi. Ispitana su svojstva: debljina premaza, tvrdoća, sjaj te prionjivost. Nakon izlaganja uzoraka u slanoj i vlažnoj komori te potapanjem u morsku vodu ispitivana su ista svojstva kao i na početnim uzorcima. Dio uzoraka prije nanošenja premaza uronjen je u fosfatnu otopinu kako bi se dodatno ispitali učinci fosfatiranja na svojstva premaza. Nakon izlaganja pločica uvjetima vlažne komore na uzorcima nisu pronađeni tragovi korozijskih produkata, pucanja niti ljuštenja prevlake. Uzorci koji su bili izloženi morskoj vodi i slanoj komori pokazali su manja oštećenja zaštitnoga premaza. Svojstvo prionjivosti ispitano je Pull-off Adhesion testom. Sila Pull-off Adhesion testa pokazuje manje vrijednosti za nefosfatirane uzorke nego za fosfatirane.
Ključne riječi (engleski)
Ključne riječi (hrvatski)
Jezikengleski
Jezikhrvatski
Vrsta publikacijeZnanstveni rad - Prethodno/kratko priopćenje
Status objaveObjavljen
Vrsta recenzijeRecenziran - međunarodna recenzija
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov časopisaRudarsko-geološko-naftni zbornik
Brojčani podacivol. 37, br. 1, str. 11-17
p-ISSN0353-4529
e-ISSN1849-0409
DOIhttps://doi.org/10.17794/rgn.2022.1.2
URN:NBNurn:nbn:hr:169:262362
Datum objave publikacije2022
URL dokumentahttps://hrcak.srce.hr/272004
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Imenovanje 4.0 međunarodna (CC BY 4.0)
Datum i vrijeme pohrane2025-04-24 08:52:53